The static recrystallization (SRX) behavior in Ti–V microalloyed steel was studied through two-pass compression tests using a Gleeble-3500 thermo-mechanical simulator. Under the experimental conditions with the deformation temperatures of 950–1050 °C, strain rates of 0.01–1 s–1, pass strains of 0.1–0.2 and inter-pass time of 1–100 s, respectively. The influence of various processing parameters on the static softening were discussed seriously and the results showed that the softening fractions raise quickly with the deformation temperature, the strain rate, the pass strain and the inter-pass time; Oppositely, it is reduced as the initial austenite grain size raises. In addition, the kinetic equations have been adopted and the required parameters have been determined based on the experiments, the calculated results are consistent with the experimental results, indicating the SRX behavior and microstructural evolutions of Ti–V microalloyed steel could be estimated by the determined kinetics parameters.

29 References.

No Supplementary Data.
No Article Media
No Metrics

Keywords: KINETICS MODEL; STATIC RECRYSTALLIZATION; TI–V MICROALLOYED STEEL; TWO-PASS HOT COMPRESSION

Document Type: Research Article

Publication date: July 1, 2020

More about this publication?
  • Materials Express is a peer-reviewed multidisciplinary journal reporting emerging researches on materials science, engineering, technology and biology. Cutting-edge researches on the synthesis, characterization, properties, and applications of a very wide range of materials are covered for broad readership; from physical sciences to life sciences. In particular, the journal aims to report advanced materials with interesting electronic, magnetic, optical, mechanical and catalytic properties for industrial applications.
  • Editorial Board
  • Information for Authors
  • Subscribe to this Title
  • Ingenta Connect is not responsible for the content or availability of external websites
  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more