Open Access The influence of hot extrusion deformation on microstructure evolution, tensile properties and corrosion behavior of Mg–3Al–0.5Mn–0.5Sr alloy

Download Article:
 Download
(PDF 27,374.5 kb)
 
A novel microalloyed Mg–3Al–0.5Mn–0.5Sr (AMJ300) alloy was designed and prepared. Then the original structure of as-cast alloy was optimized by hot extrusion. The influence of extrusion on microstructure, corrosion and tensile properties of as-cast AMJ300 alloy were studied by OM, SEM, EDS, XRD, TEM, electrochemical workstation and tensile tests. The results indicated that α-Mg, Al8Mn5 and Al4Sr phases constitute the AMJ300 alloy. Furthermore, the microstructure of alloy was further refined after extrusion, which indicates that the microstructural evolution during extrusion was governed by dynamic recrystallization. The fine and close of structure and the morphology change of intermetallic compounds greatly improved the corrosion resistance of AMJ300 alloy. The results of corrosion rate, corrosion current and corrosion morphology showed that the corrosion resistance of as-cast alloy could be significantly improved by extrusion. The main corrosion products of AMJ300 alloy in 3.5 wt.% NaCl solution was Mg(OH)2. After extrusion, the tensile properties of AMJ300 alloy was significantly improved. The tensile strength reached 349 MPa, the yield strength reached 229 MPa, and the elongation reached 13.2%. Compared with the as-cast alloy, the tensile strength, the yield strength and the elongation increased by 218.1%, 248.9% and 173.7% respectively
No References for this article.
No Supplementary Data.
No Article Media
No Metrics

Keywords: Corrosion Behavior; Extrusion; Magnesium Alloy; Microstructure; Tensile Properties

Document Type: Research Article

Affiliations: 1: School of Electronics and Internet of Things, Chongqing College of Electronic Engineering, Chongqing 401331, China 2: College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China 3: School of Materials Science and Engineering, Xi’an Polytechnic University, Shanxi 710048, China

Publication date: March 1, 2020

More about this publication?
  • Materials Express is a peer-reviewed multidisciplinary journal reporting emerging researches on materials science, engineering, technology and biology. Cutting-edge researches on the synthesis, characterization, properties, and applications of a very wide range of materials are covered for broad readership; from physical sciences to life sciences. In particular, the journal aims to report advanced materials with interesting electronic, magnetic, optical, mechanical and catalytic properties for industrial applications.
  • Editorial Board
  • Information for Authors
  • Subscribe to this Title
  • Ingenta Connect is not responsible for the content or availability of external websites
  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more