Open Access Intense broad-band absorption and efficient blue-emitting SrCa2MgSi2O8:Eu2+ phosphor for high color-rendering white LED applications

Download Article:
 Download
(PDF 3,433.2 kb)
 
New blue-emitting phosphor, SrCa2MgSi2O8:Eu2+ (SCMSO:Eu2+), was synthesized by a solid state reaction. For further discussion, a series of analysis were performed such as photoluminescence excitation and emission spectra, diffuse reflectance spectra, thermal quenching, decay lifetime and electroluminescence to identify the luminescent properties of SrCa2MgSi2O8:Eu2+ phosphors. The SCMSO:Eu2+ displays broad excitation spectra ranging from 250–450 nm, and intend emission intensity at 469 nm under λ ex = 360 nm. The optimum Eu2+ concentration of SCMSO was 10 mol%. The luminescence decay lifetimes of SCMSO:Eu2+ phosphors were measured to be 474.1–540.4 ns. The blue-emitting SrCa2MgSi2O8:10%Eu2+ phosphors fabricated with commercial red- and green-emitting phosphor integrating white LED, excited with near UV LED chip (λ ex = 390 nm), and shows excellent color rendering index. In this study, the results obtained highly indicates that SCMSO:Eu2+ is potentially blue-emitting phosphor for application in white LEDs.

41 References.

No Supplementary Data.
No Article Media
No Metrics

Keywords: FIRST PRINCIPLE CALCULATIONS; LIGHT-EMITTING DIODES (LEDS); PHOSPHOR; PHOTOLUMINESCENCE; SRCA2MGSI2O8

Document Type: Research Article

Publication date: June 1, 2018

More about this publication?
  • Materials Express is a peer-reviewed multidisciplinary journal reporting emerging researches on materials science, engineering, technology and biology. Cutting-edge researches on the synthesis, characterization, properties, and applications of a very wide range of materials are covered for broad readership; from physical sciences to life sciences. In particular, the journal aims to report advanced materials with interesting electronic, magnetic, optical, mechanical and catalytic properties for industrial applications.
  • Editorial Board
  • Information for Authors
  • Subscribe to this Title
  • Ingenta Connect is not responsible for the content or availability of external websites
  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more