Open Access Influence of growth temperature on intrinsic stress distribution in aluminum nitride grown by hydride vapor phase epitaxy

Download Article:
 Download
(PDF 2,951.9 kb)
 
Controlling stress is a fundamental issue in thin film growth, and this problem becomes more complicated in AlN film growth due to low mobility of Al adatoms. To study the evolution of intrinsic stress distribution in the beginning of growth as a function of growth temperature, AlN films were grown directly on sapphire (0001) substrates at three different growth temperatures by hydride vapor phase epitaxy (HVPE). Transmission electron microscopy (TEM) demonstrated that the intrinsic stress distribution is periodic and the period increases with the increase of temperature. At lower growth temperature, the intrinsic stresses overlap with the dislocations during the initial growth, appearing as periodic nano-sized columns perpendicular to the AlN/sapphire interface when the sample is viewed with g = 112¯0. In addition, the period is different along [11¯00] and [112¯0] for a certain temperature. With the increase of growth temperature, a large fraction of misfit dislocations bend and terminate at around 1.5 μm above the interface of AlN/sapphire forming a network. The periodicity of the stress distribution is thought to originate due to different mobilities of Al adatoms. This understanding helps to achieve stress-controllable AlN growth.
No References for this article.
No Supplementary Data.
No Article Media
No Metrics

Keywords: AL ADATOM MOBILITY; ALN; DISLOCATIONS; HVPE; INTRINSIC STRESSES

Document Type: Commentary

Publication date: August 1, 2016

More about this publication?
  • Materials Express is a peer-reviewed multidisciplinary journal reporting emerging researches on materials science, engineering, technology and biology. Cutting-edge researches on the synthesis, characterization, properties, and applications of a very wide range of materials are covered for broad readership; from physical sciences to life sciences. In particular, the journal aims to report advanced materials with interesting electronic, magnetic, optical, mechanical and catalytic properties for industrial applications.
  • Editorial Board
  • Information for Authors
  • Subscribe to this Title
  • Ingenta Connect is not responsible for the content or availability of external websites
  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more