Novel Eu2+-Activated Yellow-Emitting Sr8MgLu(PO4)7 Phosphors for White-Light Near-Ultraviolet LEDs
An Eu2+-activated Sr8MgLu(PO4)7 yellow-emitting phosphor was synthesized by a conventional solid state reaction for applications in white-light near-ultraviolet (NUV) light-emitting diodes (LEDs) having excellent color rendering index. Upon excitation at 390 nm, the Sr8MgLu(PO4)7:Eu2+ phosphor exhibits an asymmetric broad yellow emission centered at 594 nm and the composition-optimized concentration of Eu2+ in Sr8MgLu(PO4)7:Eu2+ was determined to be 0.5 mol%. The excitation spectrum of this phosphor has a broadband absorption in the 250–450 nm NUV region, which matches well with NUV chips. A white-light LED, fabricated using a NUV LED 390 nm chip pumped by a blend of yellow-emitting Sr8MgLu(PO4)7:0.005Eu2+ and blue-emitting BaMgAl10O17:Eu2+ phosphors, resulted in an excellent color rendering index of 95.4 and Commission International I'Eclairage (CIE) chromaticity coordinates of (0.336, 0.353) at a correlated color temperature of 5354 K. Based on these results, we are currently evaluating the potential application of Sr8MgLu(PO4)7:Eu2+ as a yellow-emitting near-ultraviolet convertible phosphor.
No Supplementary Data.
No Article Media
Document Type: Research Article
Publication date: December 1, 2012
More about this publication?
- Materials Express is a peer-reviewed multidisciplinary journal reporting emerging researches on materials science, engineering, technology and biology. Cutting-edge researches on the synthesis, characterization, properties, and applications of a very wide range of materials are covered for broad readership; from physical sciences to life sciences. In particular, the journal aims to report advanced materials with interesting electronic, magnetic, optical, mechanical and catalytic properties for industrial applications.
- Editorial Board
- Information for Authors
- Subscribe to this Title
- Ingenta Connect is not responsible for the content or availability of external websites