Study on the Adhesion Force Between Ga-Doped ZnO Thin Films and Polymer Substrates

Buy Article:

$106.73 + tax (Refund Policy)

Flexible Ga doped ZnO (GZO) transparent conductive thin films were prepared on polycarbonate (PC) substrates at room temperature by magnetron sputtering. The adhesive property between the GZO film and the PC substrate was investigated quantitatively by the scratch test, which is designed for the quantitative assessment of the mechanical integrity of coated surfaces. The effect of the sputtering pressures on the adhesion forces for the GZO films was investigated. When the sputtering pressure varied from 0.2 to 0.5 Pa, no obvious adhesion force alteration was observed. However, when the sputtering pressure was increased to 0.7 Pa, the adhesion force was decreased. The lowest square resistance of the GZO film was 18.6 Ω/sq. Regardless of the sputtering pressure, the transmittance in the visible light was about 90%. When the sputtering pressure was 0.4 Pa, the optimal figure of merit (ΦTC) was 2.5×10−2 Ω−1, indicating that the optimal pressure was 0.4 Pa.
No Reference information available - sign in for access.
No Citation information available - sign in for access.
No Supplementary Data.
No Article Media
No Metrics

Keywords: Adhesion Force; Flexibility; ZnO Transparent Conductive Film

Document Type: Research Article

Affiliations: 1: School of Materials Science and Engineering, Changsha University of Science and Technology, Changsha 410114, China 2: Hunan Provincial Engineering Research Center of Electric Transportation and Smart Distribution Network, Changsha University of Science and Technology, Changsha 410114, China 3: School of Metallurgy and Environment, Central South University, Changsha 410083, China

Publication date: January 1, 2019

More about this publication?
  • Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
  • Editorial Board
  • Information for Authors
  • Subscribe to this Title
  • Terms & Conditions
  • Ingenta Connect is not responsible for the content or availability of external websites
  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more