Influence of Heat Treatment on Structural and Magnetic Properties of Manganese-Cerium Mixed Iron Oxide Nanocomposites

Buy Article:

$106.34 + tax (Refund Policy)

Mn–Ce–Fe–O nanopowder was prepared by evaporation method. The results of XRD clarifying the samples are having a nanosized particles in the range ∼38–54 nm. SEM was also used to characterize the microstructure of the products. The nanostructure and particle size are confirmed by TEM. The magnetic properties of Mn–Ce–Fe–O system were measured at room temperature by using vibrating sample magnetometer (VSM). It is found that both remnant magnetization (Mr) and saturation magnetization (Ms) decrease with increasing the annealing temperature due to the decomposition of the system. The high value of saturation magnetization (Ms = 48.47 emu/g) and remnant magnetization (Mr = 20.27 emu/g) were obtained only for the asburnt sample not for annealed samples. The compositional analysis of Mn–Ce–Fe–O system was observed by energy-dispersive detection X-Ray spectra (EDXS).
No Reference information available - sign in for access.
No Citation information available - sign in for access.
No Supplementary Data.
No Article Media
No Metrics


Document Type: Research Article

Publication date: September 1, 2015

More about this publication?
  • Journal of Advanced Physics is an interdisciplinary peer-reviewed journal consolidating research activities in all experimental and theoretical aspects of advanced physics. The journal aims in publishing articles of novel and frontier physics that merit the attention and interest of the whole physics community. JAP publishes review articles, full research articles, short communications of important new scientific and technological findings in all latest research aspects of physics.
  • Editorial Board
  • Information for Authors
  • Subscribe to this Title
  • Ingenta Connect is not responsible for the content or availability of external websites
  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more