Distribution and surface characteristic of transfer film of polyamide composites filled with ZnOw during traction rolling
Purpose ‐ The purpose of this paper is to investigate the distribution and surface characteristic of transfer film of polyamide composites filled with ZnOw during traction rolling. Design/methodology/approach ‐ In this paper, the traction
rolling tribological behavior of polyamide composites filled with ZnOw was studied with a twin-disc traction rolling tester. The topography of transfer film was observed with a three dimensional profiler. Meantime the thickness of transfer film was measured. The chemistry elements of transfer
film were analyzed with EDS and XRD. Findings ‐ The results indicated that transfer film of composites patchily covered on the surface of counter disc, the amount of which increased with increasing cycles. The coverage and thickness of pure PA film increased against
rolling cycles. However, the thickness of 15?wt.% ZnOw/PA film remained at 6?ยต m as the coverage rose against rolling cycles. Fe element was found in pure PA transfer film, which existed in Fe0 and FeO for chemical reaction between Fe and atmospheric
oxygen. Transfer film of 15?wt.% ZnOw/PA composites included a little Zn and Fe element. Fe element existed as Fe0 . Zn element existed as ZnO. Originality/value ‐ This paper presented the distribution and surface characteristic of transfer film
during traction rolling.
Keywords: Polyamide composite; Polyamides; Surface properties of materials; Surface topography; Traction rolling; Transfer film
Document Type: Research Article
Publication date: 13 September 2013
- Access Key
- Free content
- Partial Free content
- New content
- Open access content
- Partial Open access content
- Subscribed content
- Partial Subscribed content
- Free trial content