High Temperature Thermomechanical Properties of Titanium-Rhodium-based Alloys Containing Scandium
At high temperatures, the equiatomic binary compounds formed by Groups 4 and 8 transition metals are known to undergo martensitic transformation, which may be accompanied by a shape memory effect. Among these compounds, titanium-rhodium (TiRh) is of special interest not only because
it undergoes two martensitic transformations at high temperature, for one of which the shape memory effect has been observed, but also because it demonstrates unusual shape recovery behaviour at temperatures higher than 400°C. The present work focuses upon the thermomechanical and mechanical
properties of 50 at% rhodium-scandium-titanium ternary alloys where Ti is substituted by Sc. These alloys were investigated for the first time using electrical resistance, dilatometry and three-point bending techniques in the temperature range 20°C to 850°C. It was found that the sample
with 0.1 at% Sc exhibited full shape restoration in the ranges of both martensitic transformations at ~340°C and ~750°C. Two-way shape recovery was also observed. A small temperature hysteresis, desirableforalloysused inactuator applications, is present in TiRh and Rh-Sc-Ti alloys.
Both TiRh and Sc-containing alloys exhibit continuity of the deformation process on cooling and shape restoration on heating in a wide range of temperatures. This feature of both TiRh and Rh-Sc-Ti alloys implies the possibility of their application in different heat-regulating elements at
temperature ranges from room temperature to 850°C.
Document Type: Research Article
Publication date: 01 January 2014
Johnson Matthey's journal of research on the platinum group metals and developments in their application in industry from 1957-2014. It has now been renamed the Johnson Matthey Technology Review
- Editorial Board
- Information for Authors
- Terms & Conditions
- Disclaimer and Copyright Notice
- Ingenta Connect is not responsible for the content or availability of external websites
- Access Key
- Free content
- Partial Free content
- New content
- Open access content
- Partial Open access content
- Subscribed content
- Partial Subscribed content
- Free trial content