Open Access Effect of Platinum Addition to Coinage Metals on Their Ultrasonic Properties

Download Article:
(HTML 46.2 kb)
(PDF 158.6 kb)
Ultrasonic attenuation for the longitudinal and shear waves due to phonon-phonon interaction and due to thermoelastic relaxation mechanisms have been evaluated in bimetallic alloys of the coinage metals (copper, silver or gold) with 1, 2, 3 or 4 at% platinum. The evaluations were carried out along the100〉, 〈111and110crystallographic directions at room temperature. Second- and third-order elastic constants, ultrasonic velocities and thermal relaxation times have also been computed for these alloys. In each case, the addition of platinum to the coinage metal reduces the attenuation, which indicates that bimetallic alloys with a higher platinum content are more ductile and stable and contain fewer defects in their crystal structure than those with a lower platinum content. The predominant mechanism of attenuation of ultrasonic waves is phonon-phonon interaction rather than thermoelastic loss. The results are compared with available theoretical data and experimental measurements for the pure coinage metals. These results, in combination with other well-known physical properties, can be applied to the non-destructive testing of materials for various industrial applications.

29 References.

No Supplementary Data.
No Article Media
No Metrics

Document Type: Research Article

Publication date: July 1, 2010

More about this publication?
  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more