Investigation of optical properties: Eu with Al codoping in aluminum silicate glasses and glass‐ceramics

Buy Article:

$52.00 + tax (Refund Policy)

Eu‐doped transparent oxyfluoride aluminosilicate glass was prepared by controlling with Al codoping of melt‐quenched glass fabricated under air atmosphere. In the presence of Al input, the photoluminescence emission spectra under 393 nm excitation shows a blue shift by adjusting the ratio of Eu3+ and Eu2+. After heat treatment of glass, the ratio of Eu3+ and Eu2+ of luminescence emission were changed by controlling treatment temperature. The PL intensity of Eu3+ and Eu2+ ions in the glass‐ceramics (GC) was much stronger than in the precursor glass (PG). The possible mechanism responsible for color tuneability of the ratio of Eu3+ and Eu2+ doped was discussed.
No References
No Citations
No Supplementary Data
No Article Media
No Metrics

Keywords: Eu3+ and Eu2+; NaYF4 nanocrystals; W‐LED quantum efficiency; glass‐ceramics; heat treatment

Document Type: Research Article

Publication date: July 1, 2017

  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more