Low Temperature Ionic Conductivity of an Acceptor‐Doped Perovskite: II. Impedance of Single‐Crystal BaTiO3

Buy Article:

$52.00 + tax (Refund Policy)

Low temperature conductivity mechanisms were identified in acceptor‐doped BaTiO3 single crystals equilibrated and quenched from high temperature under different oxygen partial pressures. A range of acceptor ionization states were quenched into samples doped with manganese or iron. Using an appropriate equivalent circuit to interpret impedance spectroscopy data, room temperature conductivity mechanisms in the single crystal samples were identified, and the permittivity/temperature dependence was also shown to be self‐consistent with the nature of a first‐order ferroelectric phase transition. The primary, low temperature, conduction mechanism in acceptor‐doped BaTiO3 was determined to be dominated by the migration of oxygen vacancies. The activation energy for oxygen vacancy migration was experimentally determined to have a value of nearly 0.7 eV. This activation energy represents an intrinsic value for vacancy hopping and confirms our previous work that revealed minimal interaction between acceptor dopants and oxygen vacancies in BaTiO3 in contrast to the well‐documented evidence of defect association in SrTiO3.
No References
No Citations
No Supplementary Data
No Article Media
No Metrics

Keywords: defects; electrical conductivity; ferroelectricity/ferroelectric materials; impedance spectroscopy; vacancies

Document Type: Research Article

Publication date: October 1, 2016

  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more