Fabrication and Microwave Dielectric Properties of Mg2SiO4‐LiMgPO4‐TiO2 Composite Ceramics

Buy Article:

$47.00 + tax (Refund Policy)

Complete solid solutions between Mg2SiO4 and LiMgPO4 are confirmed by the XRD results. The phase constitution of 0.5Mg2SiO4‐0.5LiMgPO4 is found to be dependent on firing temperature. The chemical compatibility between Mg2SiO4 and rutile phase at sintering temperature is modified by incorporating LiMgPO4. The microwave dielectric properties of (1−y)(0.5Mg2SiO4‐0.5LiMgPO4)‐yTiO2 (y = 0–0.3) composite ceramics have been investigated. The optimized microwave dielectric properties for 0.35Mg2SiO4‐0.35LiMgPO4‐0.3TiO2 ceramics sintered at 1050°C show low dielectric constant (11.4), high‐quality factor (31 800 GHz), and low‐temperature coefficient of resonant frequency (−4 ppm/°C).
No References
No Citations
No Supplementary Data
No Article Media
No Metrics

Keywords: LiMgPO4; forsterite; microwave dielectrics

Document Type: Research Article

Publication date: August 1, 2016

  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more