Synthesis and Mechanical Properties of (Ti,V)2AlC/Al2O3 In Situ Solid Solution Composites by Reactive Hot Pressing

Buy Article:

$52.00 + tax (Refund Policy)

Solid solution composites of (Ti,V)2AlC/Al2O3 were successfully synthesized using the in situ hot‐pressing process by the incorporation of the thermit reaction of Al with V2O5 in Ti, Al, and carbon black system. The phase evolution during the formation of the composites was examined from 500°C to 1350°C, and a possible reaction mechanism was proposed to explain the formation of (Ti,V)2AlC/Al2O3 solid solution composites. The composite with 10 wt% Al2O3 possesses the best mechanical properties and the hardness, flexural strength, and fracture toughness of the composites are enhanced by 53.2%, 140%, and 180%, respectively. The strengthening and toughening mechanisms were also discussed.
No References
No Citations
No Supplementary Data
No Article Media
No Metrics

Document Type: Research Article

Publication date: October 1, 2012

  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more