The Oxidation and Oxygen Permeation Resistance of Quartz Particle‐Reinforced Aluminosilicate Glass Coating on Titanium Alloy

Buy Article:

$52.00 + tax (Refund Policy)

An aluminosilicate glass coating dispersed with quartz particles was prepared on Ti811 alloy by slurry technique to study its high‐temperature performances. The coated and uncoated samples were exposed in air at 1000°C for 50 h, and then characterized using scanning electron microscopy, energy‐dispersive spectroscopy, X‐ray diffraction, and microhardness depth profile. Mass gains of the samples with and without coatings were measured during the oxidation. For the samples of Ti811 without the glass coating, thick rutile‐TiO2 scales were observed, within which several thin alumina layers presented. Typical oxygen permeation phenomenon was also observed. The mass gains of the samples with the glass coating were measured to be only about 1/10 of those of the samples without coatings, and the oxygen permeation phenomenon was prevented. A Ti5Si3/Ti3Al bilayer was observed beneath the coating, and believed to act as an oxygen diffusion barrier. In general, the quartz particle‐reinforced glass coating provided good protection of the alloy Ti811 from high‐temperature oxidation and oxygen permeation.
No References
No Citations
No Supplementary Data
No Article Media
No Metrics

Document Type: Research Article

Affiliations: State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China

Publication date: August 1, 2011

  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more