Influences of Sintering Temperature on Piezoelectric, Dielectric and Ferroelectric Properties of Li/Ta-Codoped Lead-Free (Na,K)NbO3 Ceramics

Buy Article:

$52.00 + tax (Refund Policy)

Li/Ta-codoped lead-free (Na,K)NbO3 ceramics with a nominal composition of [(Na0.535K0.480)0.942Li0.058](Nb0.90Ta0.10)O3 were synthesized normally at 1070°–1100°C. The XRD patterns of all samples show a single pervoskite structure with tetragonal symmetry. Although MPB separating the orthorhombic and tetragonal symmetries was absent, the maximum piezoelectric coefficient (d33), electromechanical coupling coefficient (kp), Curie temperature (Tc), and remanent polarization (Pr) were optimized as 216 pC/N, 38.1%, 445°C, and 8.73 C/cm2, respectively.
No References
No Citations
No Supplementary Data
No Article Media
No Metrics

Document Type: Research Article

Affiliations: 1: School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China 2: State Key Laboratory of New Ceramics and Fine Processing, Department of Materials Science and Engineering, Tsinghua University, Beijing 100084, China

Publication date: May 1, 2008

  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more