Formation Mechanism of Porous Alumina With Oriented Cylindrical Pores Fabricated by Unidirectional Solidification

Buy Article:

$52.00 + tax (Refund Policy)

Porous alumina whose pores were aligned in one direction was fabricated by the unidirectional solidification method under a pressurized hydrogen atmosphere. The porous structure is formed at the solid–liquid interface during solidification due to a hydrogen solubility gap at the melting point. The hydrogen gas is dissolved into molten alumina according to Sieverts' law and insoluble gas that corresponds to the amount of solubility gap evolves from the solid phase at the solid–liquid interface during the unidirectional solidification to form the pores. The porosity and pore size of the solidified samples decreased with increasing total pressure where the environmental gas consisted of pure hydrogen or hydrogen–argon mixed gases. There is a reverse proportion relation between the pore diameter and the total pressure according to Boyle's law.
No References
No Citations
No Supplementary Data
No Article Media
No Metrics

Document Type: Research Article

Affiliations: The Institute of Scientific and Industrial Research, Osaka University, Ibaraki 567-0047, Japan

Publication date: January 1, 2008

  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more