Zirconia–Mullite Composites Consolidated by Spark Plasma Reaction Sintering from Zircon and Alumina

Buy Article:

$52.00 + tax (Refund Policy)

Mullite–ZrO2 composites have been fabricated by attrition milling a powder mixture of zircon, alumina, and aluminum metal with MgO or TiO2 as sintering additives, heating at 1100°C to oxidize the aluminum metal, and consolidation by spark plasma sintering (SPS). The influence of the SPS temperature on the formation of mullite, and the density and the mechanical properties of the resulting composites have been studied. For the mullite–zirconia composites without sintering additives, the mullite formation was accomplished at 1540°C. In contrast, for the composites having MgO and TiO2, the formation temperature dropped to 1460°C. The composites without sintering additives were almost fully dense (99.9% relative density) and retained a larger amount of tetragonal zirconia. Those materials attained the best mechanical properties (E=214 GPa and KIC=6 MPa·m1/2). To highlight the advantages of using the SPS technique, the obtained results have been compared with the characteristics of a mullite–zirconia composite prepared by the conventional reaction-sintering process.
No References
No Citations
No Supplementary Data
No Article Media
No Metrics

Document Type: Research Article

Affiliations: 1: Department of Materials, Metropolitan Autonomous University-Atzcapotzalco, Mexico, D.F., 02200 Mexico 2: CIITEC, National Polytechnic Institute, Mexico D.F., 07300, Mexico 3: Toyohashi University of Technology, Toyohashi, Japan 4: Technology Research Institute of Osaka Prefecture, Izumi, Osaka 594-1154, Japan 5: Department of Metallurgical and Materials Engineering, National Polytechnic Institute, Mexico, D.F., 07300 Mexico

Publication date: May 1, 2005

  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more