Catalyst-Free Patterned Growth of Well-Aligned ZnO Nanowires on ITO Substrates Using an Aqueous Solution Method and Lithography Process

Buy Article:

$106.67 + tax (Refund Policy)

Well-aligned ZnO nanowires were directly grown on indium tin oxide (ITO) glass substrates coated with ZnO seed layers via an aqueous solution route. During the growth process, the ZnO seed layer played the role of providing nucleation sites in the selective growth of the well-aligned ZnO nanowires. The ZnO seed layer was deposited on the substrate using pulsed laser deposition (PLD) at room temperature. The uniform ZnO nanowires were grown in aqueous solution containing zinc nitrate hexahydrate and hexamethylenetetramine at 90 °C. The diameter and length of ZnO nanowires were approximately 80 nm and 2.2 m, respectively. The selectively patterned ZnO nanowires were fabricated on the ITO-coated substrates by combining this simple solution method and a conventional photolithography process.
No Reference information available - sign in for access.
No Citation information available - sign in for access.
No Supplementary Data.
No Article Media
No Metrics


Document Type: Research Article

Publication date: August 1, 2010

More about this publication?
  • Journal of Nanoelectronics and Optoelectronics (JNO) is an international and cross-disciplinary peer reviewed journal to consolidate emerging experimental and theoretical research activities in the areas of nanoscale electronic and optoelectronic materials and devices into a single and unique reference source. JNO aims to facilitate the dissemination of interdisciplinary research results in the inter-related and converging fields of nanoelectronics and optoelectronics.
  • Editorial Board
  • Information for Authors
  • Subscribe to this Title
  • Ingenta Connect is not responsible for the content or availability of external websites
  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more