Synthesis and Characteristics of Large-Area and High-Filling CdS Nanowire Arrays in AAO Template

CdS nanowires arrays were successfully synthesized by a simple solvothermal process using AAO as templates. The phase structures, morphologies, and optical properties of the products were investigated by X-ray diffraction, scanning electron microscopy, high-resolution transmission electron microscopy, Raman spectroscopy, and photoluminescence spectroscopy. It was found that the nanowires were composed of hexagonal structure CdS nanoparticles and the average diameters is about 60–70 nm. A strong green emission with a maximum around 505 nm was observed from the synthesized CdS nanowires at room temperature, which was attributed to near-band-edge emission. A 3D self-seed nucleation coalescent process was proposed for the formation of CdS nanowires structures. The present synthetic route is expected to be applied to the synthesis of other II–VI groups or other group’s 1D semiconducting materials.