Improvement in the Positive Bias Temperature Stability of SnO x -Based Thin Film Transistors by Hf and Zn Doping

Buy Article:

$107.14 + tax (Refund Policy)

We investigated the performance of tin oxide thin film transistors (TFTs) using DC magnetron sputtering. A remarkable improvement in the transfer characteristics was obtained for the Hf-doped tin oxide (HTO) TFT. We also developed amorphous hafnium-zinc-tin oxide (HZTO) thin film transistors and investigated the effects of hafnium doping on the electrical characteristics of the HTO TFTs. Doping with hafnium resulted in a reduced defect density in the tin oxide channel layer related to oxygen vacancies, which may result from increased field effect mobility. Zinc atoms have relatively higher oxidation potential compared to tin atoms, so more oxygen molecules can be absorbed and more electrons are trapped in the HZTO films. The HZTO TFTs exhibited good electrical characteristics with a field effect mobility of 10.98 cm2/Vs, and a high ION/IOFF ratio over 108.

Document Type: Research Article

Publication date: October 1, 2015

More about this publication?
  • Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
  • Editorial Board
  • Information for Authors
  • Subscribe to this Title
  • Terms & Conditions
  • Ingenta Connect is not responsible for the content or availability of external websites
  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content