Investigation of the Dielectric Function of Solution-Processed InGaZnO Films Using Ellipsometry

Buy Article:

$107.14 + tax (Refund Policy)

The optical properties of InGaZnO (IGZO) films grown through the sol-gel process as a function of sintering time were investigated with spectroscopic ellipsometry (SE). The IGZO precursor sol was prepared by mixing In nitrate, Ga nitrate, and Zn acetate at a molar ratio of In:Ga:Zn = 3:1:1. The solution was deposited on a SiO2/Si substrate via spin coating. Sintering was performed at 400 °C for 1-15 h in an ambient atmosphere. The optical properties were measured over the range 1.12-6.52 eV via variable angle SE, at room temperature. The angle of incidence was varied from 50 to 70° in 5° steps. To extract the pure optical properties of IGZO, multilayer-structure calculation with Tauc-Lorentz dispersion relation for IGZO was performed. The changes in the dielectric function of the IGZO films with varying sintering time were observed. The resultant optical properties can be related to the concentration of oxygen vacancies in the material, which can be controlled by the sintering time.

Document Type: Research Article

Publication date: July 1, 2012

More about this publication?
  • Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
  • Editorial Board
  • Information for Authors
  • Subscribe to this Title
  • Terms & Conditions
  • Ingenta Connect is not responsible for the content or availability of external websites
  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content