Highly Ordered Poly(thiophene)s Prepared in Mesoporous Silica Nanoparticles
Nanostructured PEDOT was synthesized using mesoporous silica as a nano-template. The polymerization of thiophene monomers was performed with an oxidant and mesoporous silica nanoparticles. The silica particles took essential role in absorbing monomers and oxidant molecules, and growth
of polymers inside their pores. As prepared polymer/silica composite was treated with HF solution to remove silica template to result in 1D wire structure and mesh type porous 3D structures from SBA-15 and KIT-6 template, respectively. The average size of the poly(thiophene) wires was 10∼15
nm, which was matched well to the pores size of the silica templates, as determined from an electron microscopy. At optimized condition, the room temperature electrical conductivities of the PEDOT grown from SBA-15 and KIT-6 template were similar as 1.1 and 1.0 S/cm, respectively. However,
the evolution of the PEDOT conductivity versus temperature was different depending on the templates. These results gave a unique chance to tailor made 3 dimensional structure as well as properties of conductive polymer.
Keywords: CONDUCTIVE POLYMER; KIT; NANOSTRUCTURE; POLY(THIOPHENE); SBA; SILICA NANO TEMPLATE
Document Type: Research Article
Publication date: 01 May 2011
- Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
- Editorial Board
- Information for Authors
- Subscribe to this Title
- Terms & Conditions
- Ingenta Connect is not responsible for the content or availability of external websites
- Access Key
- Free content
- Partial Free content
- New content
- Open access content
- Partial Open access content
- Subscribed content
- Partial Subscribed content
- Free trial content