Effect of Thermal Annealing on the Efficiency of Heterojunction Photovoltaic Cells Fabricated Using Poly(3-hexylthiophene) and Methanofullerene, [6,6]-Phenyl C61-Butyric Acid Methyl Ester
The effects of thermal annealing on the efficiency of heterojunction photovoltaic (PV) cells that were fabricated using poly(3-hexylthiophene) (P3HT) and methanofullerene, [6,6]-phenyl C61-butyric acid methyl ester (PCBM) were investigated. The absorption spectra showed that the absorption
intensity of the P3HT:PCBM layer that was annealed for 5 min had the highest value among the several samples with different annealing temperatures. The atomic force microscopy image showed that the P3HT:PCBM layer that was annealed for 5 min had the best surface morphology. The X-ray photoelectron
spectroscopy demonstrated that the P3HT:PCBM layer that was annealed at 140 °C for 10 min enhanced the PCBM aggregation on the surface Al layer that was covered by the P3HT:PCBM layer. The efficiencies of the PV cells that were annealed at 3, 5, and 10 min were approximately 2.7, 4.2,
and 3.5%, respectively. Based on the experiment results, the variations in the efficiency of the PV cells due their thermal treatment were described.
Document Type: Research Article
Publication date: 01 July 2012
- Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
- Editorial Board
- Information for Authors
- Subscribe to this Title
- Terms & Conditions
- Ingenta Connect is not responsible for the content or availability of external websites
- Access Key
- Free content
- Partial Free content
- New content
- Open access content
- Partial Open access content
- Subscribed content
- Partial Subscribed content
- Free trial content