Field Emission Study of Carbon Nanotubes Forest and Array Grown on Si Using Fe as Catalyst Deposited by Electro-Chemical Method
Vertically aligned carbon nanotubes are synthesized by Low Pressure Chemical Vapor Deposition (LPCVD) on Si substrate coated with Fe as a catalyst at a pressure of 20 Torr and at a growth temperature of 600 °C. The catalyst film is prepared by electro-chemical method which is very unique and a low cost method. Three precursor gases Acetylene (C2H2), Ammonia (NH3) and Hydrogen (H2) at the flow rate of 20 sccm, 100 sccm and 100 sccm respectively are allowed to flow through the Low Pressure Chemical Vapor Deposition reactor for 10 minutes. Scanning Electron Microscope (SEM) images show that synthesized CNTs are vertically aligned and uniformly distributed with a high density. Raman analysis shows G-band at 1574 cm−1 and D-band at 1370 cm−1. The G-band is higher than D-band, which indicates that CNTs are highly graphitized. The field emission measurement reveals good field emission properties of as-grown vertically aligned carbon nanotubes with turn-on field of 1.91 V/μm at the current density 10 mA/cm2. The field enhancement factor is calculated to be 7.82 × 103 for as-grown carbon nanotubes.
No Reference information available - sign in for access.
No Citation information available - sign in for access.
No Supplementary Data.
No Article Media
Document Type: Research Article
Publication date: 01 March 2012
More about this publication?
- Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
- Editorial Board
- Information for Authors
- Subscribe to this Title
- Terms & Conditions
- Ingenta Connect is not responsible for the content or availability of external websites