Inkjet-Printing of Antimony-Doped Tin Oxide (ATO) Films for Transparent Conducting Electrodes
Antimony-doped Tin oxide (ATO) films have been prepared by inkjet-printing method using ATO nanoparticle inks. The electrical and optical properties of the ATO films were investigated in order to understand the effects of rapid thermal annealing (RTA) temperatures. The decrease in the
sheet resistance and resistivity of the inkjet-printed ATO films was observed as the annealing temperature increased. The film annealed at 700 °C showed the sheet resistance of 1.7 × 103 Ω/sq with the film thickness of 350 nm. The optical transmittance of the films
remained constant regardless of their annealing temperatures. In order to further reduce the sheet resistance of the films as well as the annealing temperature, Ag-grid was printed in between two layers of inkjet-printed ATO. With 1.5 mm Ag line spacing, the Ag-grid embedded ATO film showed
the sheet resistance of 25.6 Ω/sq after RTA at 300 °C.
Keywords: ATO; INKJET PRINTING; NANOPARTICLES; TCO
Document Type: Research Article
Publication date: 01 February 2012
- Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
- Editorial Board
- Information for Authors
- Subscribe to this Title
- Terms & Conditions
- Ingenta Connect is not responsible for the content or availability of external websites
- Access Key
- Free content
- Partial Free content
- New content
- Open access content
- Partial Open access content
- Subscribed content
- Partial Subscribed content
- Free trial content