Properties of Metakaolin Geopolymeric Binder

Buy Article:

$105.00 plus tax (Refund Policy)

This paper investigates the physical and mechanical properties as well as the morphology study of the MK geopolymeric binder. Mixture of waterglass liquid and NaOH solution were used as the activator solution for the activation of MK. The slurry was oven-heated to obtain solidified paste. It was then pulverized to obtain the geopolymeric binder. For testing, this geopolymeric binder was mixed with water (≈22%) to form resulted geopolymer paste. The results indicated that the surface area of the MK geopolymeric binder was 9.76 m2/g. The resulted geopolymer paste set in 420 minutes at 60 °C. The bulk density of the resulted geopolymer paste was low (1000 kg/m3–1300 kg/m3). The compressive strength of resulted MK geopolymer paste increased over age and the strength at 28 days was 9.58 MPa. In addition, the microstructures of the resulted geopolymer pastes displayed the increase of the spherical aggregates of geopolymer gel and the densification of the structure, which complied with the increasing strength.
No Reference information available - sign in for access.
No Citation information available - sign in for access.
No Supplementary Data.
No Article Media
No Metrics

Document Type: Research Article

Publication date: 2013-01-01

More about this publication?
  • ADVANCED SCIENCE LETTERS is an international peer-reviewed journal with a very wide-ranging coverage, consolidates research activities in all areas of (1) Physical Sciences, (2) Biological Sciences, (3) Mathematical Sciences, (4) Engineering, (5) Computer and Information Sciences, and (6) Geosciences to publish original short communications, full research papers and timely brief (mini) reviews with authors photo and biography encompassing the basic and applied research and current developments in educational aspects of these scientific areas.
  • Editorial Board
  • Information for Authors
  • Subscribe to this Title
  • Ingenta Connect is not responsible for the content or availability of external websites
  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more