Effects induced by γ-irradiation on intraband transitions in Sr2+-doped ammonium zinc chloride crystals
Considerable changes were observed in the X-ray diffraction pattern of ammonium zinc chloride after doping with Sr2+ in different concentrations and after irradiating with γ rays at different doses. The effect of γ-radiation and Sr2+ content on
optical parameters of (NH4)2ZnCl4: x Sr2+ single crystals (x = 0.00, 0.020, 0.039, 0.087 or 0.144 wt.%) has been investigated. The transmittance near the absorption edge of unirradiated crystals and crystals
irradiated with different γ-doses has been measured, hence the absorption coefficient (α) was calculated. The values of α at room temperature increased under the influence of γ-irradiation. The rate by which α increases with photon energy just before the absorption
edge is strongly inhibited by higher γ-doses. The type of intraband transition in (NH4)2ZnCl4: x Sr2+ single crystals was found to be of the allowed indirect transition, and γ-irradiation had no effect on the type of transition.
The values of the optical energy gap (E
g
) were calculated as a function of γ-dose. The effect of γ-irradiation was found to be more pronounced on samples doped with x = 0.087 or 0.144 wt.% Sr2+. The results can be
discussed on the basis of γ-irradiation-induced defects and Sr2+ concentration. A diagram representing probable transitions to the created bands due to irradiation could be constructed.
Document Type: Research Article
Affiliations: 1: The American University in Cairo Physics Department, School of Science and Engineering Cairo 11511 Egypt 2: Assiut University Physics Department, Faculty of Science 71516 Assiut Egypt
Publication date: 01 November 2003
- Access Key
- Free content
- Partial Free content
- New content
- Open access content
- Partial Open access content
- Subscribed content
- Partial Subscribed content
- Free trial content