ELECTRO-OPTIC EFFECTS OF La-MODIFIED PMN-PT THIN FILMS FOR WAVEGUIDE APPLICATIONS

Buy Article:

$55.00 plus tax (Refund Policy)

Lanthanum-modified lead magnesium niobate titanate (PLMNT) thin films were fabricated on glass, silicon and sapphire substrates successfully via a chemical solution deposition process. The PLMNT thin films exhibited large electro-optic (EO) coefficients with La concentrations between 2.0-2.5 mol%. The largest EO coefficient was measured in a PLMNT thin film about 1  m thick deposited on r-cut sapphire substrate. The effective EO coefficient r31 measured at 532 nm was as large as 1079 pm/V.
No Reference information available - sign in for access.
No Citation information available - sign in for access.
No Supplementary Data.
No Data/Media
No Metrics

Keywords: PMN-PT; chemical solution deposition; electro-optic; thin films; waveguide

Document Type: Research Article

Affiliations: Boston Applied Technologies, Inc., Woburn, Massachusetts, USA

Publication date: 2008-01-01

More about this publication?
  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more