ELECTRICAL PROPERTIES OF ULTRASONIC NOZZLE USING MULTILAYER LOW TEMPERATURE SINTERING Pb(Mn1/3Nb2/3)O3-Pb(Ni1/3Nb2/3) O3-Pb(Zr0.50Ti0.50)O3 CERAMICS
The multilayer ring type piezoelectric vibrator was manufactured using low temperature sintering Pb(Mn1/3Nb2/3)O3-Pb(Ni1/3Nb2/3)O3-Pb(Zr0.50Ti0.50)O3 (abbreviate ed as PMN-PNN-PZT) piezoelectric ceramic added Na2CO3 and Li2CO3 as sintering aids. And then, ultrasonic nozzle was fabricated using the vibrator. The driving current and driving power of the ultrasonic nozzle showed the stable values as 260 mA and 8.1W after 10 min operation. No problems were occurred even under long time operation because the surface temperature of the ceramic actuator kept the maximum value of 26°C in the experiment.
Keywords: low temperature sintering; multilayer ring type piezoelectric vibrator; ultrasonic nozzle
Document Type: Research Article
Affiliations: Department of Electrical Engineering, Semyung University, Jecheon, Chungbuk, Korea
Publication date: 01 January 2008
- Information for Authors
- Subscribe to this Title
- Ingenta Connect is not responsible for the content or availability of external websites
- Access Key
- Free content
- Partial Free content
- New content
- Open access content
- Partial Open access content
- Subscribed content
- Partial Subscribed content
- Free trial content