Calibration of Raman Spectroscopy in the Stress Measurement of Air-Plasma-Sprayed Yttria-Stabilized Zirconia

$29.00 plus tax (Refund Policy)

Buy Article:

Abstract:

Thermal barrier coatings (TBC) are used widely on a range of components that operate at high temperatures. We report measurement of the factor that is required to convert the Raman shift to stress for air plasma sprayed yttria (7 wt %) stabilized tetragonal zirconia (ZrO2) (YSZ) thermal barrier coatings. The factor is evaluated for the as-coated condition and also following a heat treatment at 1000 °C for 1050 h. Two Raman bands at 608 cm−1 and 640 cm−1 have been investigated in a diamond anvil cell under hydrostatic pressure up to ∼24 GPa. In the range of zero to ∼1.6 GPa, a linear behavior was observed in terms of the shifts of these two Raman bands with a gradient similar to dense bulk tetragonal ZrO2. From these measurements the factors to convert wavenumber shift to stress have been derived. The application of these conversion factors to stress measurement in TBC coated test specimens and components is discussed.

Keywords: Air plasma spray; Conversion factor; Raman spectroscopy; Stress; Tetragonal yttria-stabilized zirconia

Document Type: Research Article

DOI: http://dx.doi.org/10.1366/12-06676

Affiliations: Interface Analysis Centre, University of Bristol, Bristol BS2 8BS, UK

Publication date: October 1, 2012

More about this publication?
Related content

Tools

Favourites

Share Content

Access Key

Free Content
Free content
New Content
New content
Open Access Content
Open access content
Subscribed Content
Subscribed content
Free Trial Content
Free trial content
Cookie Policy
X
Cookie Policy
ingentaconnect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more