Dependence of Surface-Enhanced Infrared Absorption (SEIRA) Enhancement and Spectral Quality on the Choice of Underlying Substrate: A Closer Look at Silver (Ag) Films Prepared by Physical Vapor Deposition (PVD)

$29.00 plus tax (Refund Policy)

Buy Article:


Silver (Ag) films of varying thickness were simultaneously deposited using physical vapor deposition (PVD) onto six infrared (IR) substrates (BaF2, CaF2, Ge, AMTIR, KRS-5, and ZnSe) in order to correlate the morphology of the deposited film with optimal SEIRA response and spectral band symmetry and quality. Significant differences were observed in the surface morphology of the deposited silver films, the degree of enhancement provided, and the spectral appearance of para-nitrobenzoic acid (PNBA) cast films for each silver-coated substrate. These differences were attributed to each substrate's chemical properties, which dictate the morphology of the Ag film and ultimately determine the spectral appearance of the adsorbed analyte and the magnitude of SEIRA enhancement. Routine SEIRA enhancement factors (EFs) for all substrates were between 5 and 150. For single-step Ag depositions, the following ranking identifies the greatest SEIRA enhancement factor and the maximum absorption of the 1345 cm−1 spectral marker of PNBA at the optimal silver thickness for each substrate: BaF2 (EF = 85 ± 19, 0.059 A, 10 nm Ag) > CaF2 (EF = 75 ± 30, 0.052 A, 10 nm Ag) > Ge (EF = 45 ± 8, 0.019 A, 5 nm Ag) > AMTIR (EF = 38 ± 8, 0.024 A, 15 nm Ag) > KRS-5 (EF = 24 ± 1, 0.015 A, 12 nm Ag) > ZnSe (EF = 9 ± 5, 0.008 A, 8 nm Ag). A two-step deposition provides 59% larger EFs than single-step depositions of Ag on CaF2. A maximum EF of 147 was calculated for a cast film of PNBA (surface coverage = 341 ng/cm2) on a 10 nm two-step Ag film on CaF2 (0.102 A, 1345 cm−1 symmetric NO2 stretching band). The morphology of the two-step Ag film has smaller particles and greater particle density than the single-step Ag film.


Document Type: Research Article


Affiliations: 1: Dept. of Chemistry and Physics and USC NanoCenter, University of South Carolina Aiken, Aiken, South Carolina 29801, USA 2: Savannah River National Laboratory, Aiken, South Carolina 29808, USA 3: Dept. of Physics and Astronomy and USC NanoCenter, University of South Carolina, Columbia, South Carolina 29208, USA

Publication date: March 1, 2011

More about this publication?
Related content



Share Content

Access Key

Free Content
Free content
New Content
New content
Open Access Content
Open access content
Subscribed Content
Subscribed content
Free Trial Content
Free trial content
Cookie Policy
Cookie Policy
ingentaconnect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more