Transformation of the Near-Infrared Bands of Cellulose Surface Hydroxyls under the Influence of Adsorbed Water Molecules

$29.00 plus tax (Refund Policy)

Buy Article:


Near-infrared absorption spectra of sulfite cellulose with a varied adsorbed water content were studied. Analysis of the spectra has been made on the basis of previously published relations and results of the cellulose surface hydroxyls' interaction with absorbed water. Spectra of the OH overtone region of 1.3-1.65 mu m were deconvoluted to components of cellulose volume and surface hydroxyls as well as to those of absorbed water. Besides the 1.53-1.55 mu m component of ''bound'' water, the 1.42-1.44 mu m component of ''free'' water starts to grow as the surface coverage exceeds 1.5. Comparison of the peak positions of these water components with those of liquid water suggests that bound water is constituted of hydrogenbonded molecules. The 1.42-1.44 mu m component of free water implies nonhydrogen-bonded and partially hydrogen-bonded molecules. The whole 1.363 mu m band and a part of the 1.424 mu m band of surface hydroxyls turn into the 1.52-1.53 and 1.57-1.59 mu m peaks, respectively, after attachment of H O molecules. The red shift of the surface bands by approximately 780cm -1 caused by the adsorbate is consistent with a shift of the fundamental OH band of silica gel. The possible chemical, morphological, and physical causes of the two 1.363 and 1.424 mu m surface hydroxyl bands are discussed. Index Headings: Near-infrared; Absorption spectra; Cellulose; Absorbed water; Bands of surface hydroxyls.

Document Type: Research Article


Publication date: March 1, 2000

More about this publication?
Related content



Share Content

Access Key

Free Content
Free content
New Content
New content
Open Access Content
Open access content
Subscribed Content
Subscribed content
Free Trial Content
Free trial content
Cookie Policy
Cookie Policy
ingentaconnect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more