The Chemical Interaction of Organic Materials with Metal Substrates. Part I: ESCA Studies of Organic Phosphate Films on Steel

Authors: Schuetzle, D.1; Carter, R. O.1; Shyu, J.1; Dickie, R. A.1; Holubka, J.1; McIntyre, N. S.2

Source: Applied Spectroscopy, Volume 40, Issue 5, Pages 583-716 (July 1986) , pp. 641-649(9)

Publisher: Society for Applied Spectroscopy

Buy & download fulltext article:

OR

Price: $29.00 plus tax (Refund Policy)

Abstract:

ESCA and ellipsometry have been used to determine the film thickness, molecular orientation, and chemical bonding of an organic phosphate on polished steel substrates. The organic phosphate studied was formed as a reaction product of one mole of the diglycidyl ether of bis-phenol-A (DGEBA) with two moles of phosphoric acid, and comprised the monoand diphosphate adducts of DGEBA. The steel substrates were found to bear an iron oxide layer that was 19 ± 4 Å in thickness as determined with the use of angle-resolved ESCA depth analysis. Ellipsometry measurements gave an iron oxide thickness of 26 ± 3 Å. Surface treatment of steel with the organic phosphate homogeneously covered the surface with 30 ± 5 Å of the coating as determined with the use of the ESCA depth analysis. The phosphate end-groups of the organic phosphate were concentrated at the coating/iron oxide interface. A shift in the phosphorus (2p) spectra from 135.2 to 134.2 eV was observed when the organic phosphate coating bonded to the iron oxide substrate. The binding energy of 134.2 eV was close to that observed for an iron organo-phosphate reference material at 134.0 eV. A shift in the iron (2p) spectra from 711.0 to 711.7 eV at a sampling depth of approximately 35 Å indicates the possible formation of an iron organic phosphate at the iron oxide/coating interface. The carbon and oxygen spectra confirmed the spatial orientation of the organic phosphate on the surface.

Keywords: ESCA; Molecular structure; Surface analysis; XPS

Document Type: Research Article

DOI: http://dx.doi.org/10.1366/0003702864508548

Affiliations: 1: Research Staff, Ford Motor Company, Dearborn, Michigan 48121 2: Surface Science Western, University of Western Ontario, London, Ontario N6A 5B7, Canada

Publication date: July 1, 1986

More about this publication?
Related content

Tools

Key

Free Content
Free content
New Content
New content
Open Access Content
Open access content
Subscribed Content
Subscribed content
Free Trial Content
Free trial content

Text size:

A | A | A | A
Share this item with others: These icons link to social bookmarking sites where readers can share and discover new web pages. print icon Print this page