Mechano-chemical effects on surface properties and molybdate exchange on hydrotalcite

Buy Article:

$13.61 plus tax (Refund Policy)

Abstract:

The effects of mechano-chemical treatment on the surface characteristics and sorption properties of hydrotalcite were studied. Non-milled (crushed) and milled samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), particle size analysis and specific area. A milling time of 2 h decreased the particle size of the hydrotalcite samples from 21 to 8.0 nm, the specific area from 97 to 5.7 m2 g–1 and the total pore volume from 0.41 to 0.01 cm3. After the crushed and milled samples had been separately calcined at 500ºC, they were agitated with 10–2 M Na2MoO4 aqueous solutions for 48 h. The molybdate ion content in the regenerated non-milled hydrotalcite samples (HTc-MoO4) was found to be 6.0 meq g–1 while in the milled hydrotalcite (HTm-MoO4) samples this content was 2.5 meq g–1. The lower molybdate content was thought to be a result of compaction and, hence, reduced reactivity of the milled HT samples.

Keywords: CHARACTERIZATION METHODS; HYDROTALCITE; LAYERED DOUBLE HYDROXIDE; LDH; MECHANO-CHEMICAL; MOLYBDATE; SORPTION; SURFACES

Document Type: Research Article

DOI: http://dx.doi.org/10.1180/claymin.2009.044.3.311

Publication date: September 1, 2009

More about this publication?
minsoc/cm/2009/00000044/00000003/art00004
dcterms_title,dcterms_description,pub_keyword
6
5
20
40
5

Access Key

Free Content
Free content
New Content
New content
Open Access Content
Open access content
Subscribed Content
Subscribed content
Free Trial Content
Free trial content
UA-1313315-23
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more