Authors: Hosseinpouri, M.; Mirmonsef, S.A.; Soltanieh, M.

Source: Canadian Metallurgical Quarterly, Volume 46, Number 2, June 2007 , pp. 139-143(5)

Publisher: Maney Publishing

Abstract:

Aluminum-titanium master alloys were prepared with an aluminothermic reduction of titanium dioxide dissolved in cryolite (NaF/AlF₃ = 2.5 molar ratio)-alumina melts in the presence of aluminum. The effects of time, the concentration of the titanium dioxide and temperature were investigated by spectrophotometer, scanning electron microscopy (SEM) and X-ray diffraction (XRD) techniques. Al-Ti alloys containing about 7.8 wt% Ti were prepared at T=1120 °C after 10-15 minutes reduction time. The results showed that the reduction reaction occurred very quickly, i.e., within a few minutes. It was found that the reduction product at room temperature was a master alloy composed of an aluminum matrix and a TiAl₃ intermediate phase with needle shape. The reduction product was in fact a composite.

French
On a préparé des alliages-mères d'aluminium-titane par réduction aluminothermique du dioxyde de titane dissout dans la cryolithe (NaF/AlF₃ = rapport molaire de 2.5)-bains d'alumine en présence d'aluminium. On a étudié les effets de la durée, de la concentration de dioxyde de titane et de la température au moyen des techniques de spectrophotométrie, de microscopie électronique à balayage (SEM) et de diffraction des rayons X (XRD). On a préparé un alliage d'Al-Ti contenant environ 7.8% en poids de Ti à T = 1120 °C après une durée de réduction de 10-15 minutes Les résultats montrent que la réaction de réduction s'est produite très rapidement, i.e. dans à peine quelques minutes. On a trouvé que le produit de réaction à la température de la pièce était un alliage-mère composé d'une matrice d'aluminium et d'une phase intermédiaire de TiAl₃ en forme d'aiguille. Le produit de la réduction était en fait un composite.

Document Type: Research Article

DOI: http://dx.doi.org/10.1179/000844307794535579

Publication date: 2007-06-01

More about this publication?

• Editorial Board
• Information for Authors
• Submit a Paper
• Subscribe to this Title
• Membership Information
• Information for Advertisers
• Terms & Conditions
• Top Articles
• MSE Spotlight
• Special issues
• ingentaconnect is not responsible for the content or availability of external websites

Related content

• In this: publication
• By this: publisher
• In this Subject: Mining & Metallurgy
• By this author: Hosseinpouri, M. ;  Mirmonsef, S.A. ;  Soltanieh, M.

Website © Publishing Technology. Article copyright remains with the publisher, society or author(s) as specified within the article.

• Terms and conditions
• Privacy policy
• Information for advertisers