Authors: SHABESTARI, S.G.; MALEKAN, M.

Source: Canadian Metallurgical Quarterly, Volume 44, Number 3, 2005 , pp. 305-312(8)

Publisher: Maney Publishing

Abstract:

In the metal casting industry, an improvement of component quality depends mainly on better control over the production parameters. Thus, a thermal analysis cooling curve of the alloy is used for process control in the aluminum casting industry. In this research, the effect of seven different cooling rates on the microstructure and solidification parameters of the 319 aluminum alloy have been investigated by means of thermal analysis. In each case, the cooling curve and its first derivative curve have been plotted by using very accurate thermal analysis equipment. The effect of different cooling rates on solidification parameters such as nucleation temperature (TN,α), nucleation undercooling (ΔTN,α), recalescence temperature (TR,α), solidification range (ΔTs) and total solidification time (tf) has been studied in the liquidus region. Microstructural evaluation has been carried out and DAS was measured in all solidification conditions.

Dans l’industrie de coulage des métaux, une amélioration de la qualité d’une composante dépend principalement d’un meilleur contrôle des paramètres de production. Ainsi, une analyse thermique de la courbe de refroidissement de l’alliage est utilisé pour le contrôle de procédé dans l’industrie de coulage de l’aluminium. Dans cette recherche, on a utilisé l’analyse thermique pour étudier l’effet de sept différents taux de refroidissement sur la microstructure et sur les paramètres de solidification de l’alliage d’aluminium 319. Dans chaque cas, on a tracé la courbe de refroidissement ainsi que la courbe de sa première dérivée en utilisant de l’équipement très précis d’analyse thermique. On a étudié, dans la région du liquidus, l’effet de différents taux de refroidissement sur les paramètres de solidification comme la température de nucléation (T_N,α), la surfusion de nucléation (ΔTN,_α), la température de recalescence (T_R,α) l’étendue de la solidification (ΔT_s) et la durée totale de solidification (tf). On a effectué une évaluation de la microstructure et l’on a mesuré DAS sous toutes les conditions de solidification.

Document Type: Research Article

DOI: http://dx.doi.org/10.1179/000844305794409409

Publication date: 2005-01-01

More about this publication?

• Editorial Board
• Information for Authors
• Submit a Paper
• Subscribe to this Title
• Membership Information
• Information for Advertisers
• Terms & Conditions
• Top Articles
• MSE Spotlight
• Special issues
• ingentaconnect is not responsible for the content or availability of external websites

Related content

• In this: publication
• By this: publisher
• In this Subject: Mining & Metallurgy
• By this author: SHABESTARI, S.G. ;  MALEKAN, M.

Website © Publishing Technology. Article copyright remains with the publisher, society or author(s) as specified within the article.

• Terms and conditions
• Privacy policy
• Information for advertisers