Primary recrystallization during the creep of alumina

Authors: Crosby, A.; Evans, P.E.

Source: Canadian Metallurgical Quarterly, Number 1, January-March 1974 , pp. 297-301(5)

Buy & download fulltext article:

Price: $25.00 plus tax (Refund Policy)

Abstract:

Polycrystalline alumina prepared by cold isostatic compaction and sintering has been deformed in compression in the temperature range 1600 – 1700°C and at a stress of 3000 p.s.i. The strain-time curves indicated that under these conditions recrystallization may be initiated at strains as low as 1/4-1/2%. Metallographic examination of the deformed specimens revealed directly the initial stages of recrystallization. Preferential nucleation occurred at, or near, grain boundaries and the tips of microcracks. A mechanism involving the polygonization of dislocations in highly deformed regions of the crystals is proposed as a likely nucleation process.

Résumé

De l'alumine polycristalline préparée par compaction isostatique à froid et frittage a été déformée en compression sous une contrainte de 3000 psi dans un intervalle de température de 1600° à 1700°c. Les courbes déformation-temps indiquent que dans ces conditions la recristallisation peut débuter à des déformations aussi faibles que 1/4-1/2 %. Un examen métallographiq ue des échantillons déformés révèle directement les premiers stades de la recristallisation. Une germination préférentielle se produit aux (ou près des) joints de grains ainsi qu'à la pointe des microfissures. Comme interprétation possible de cette germination, les auteurs proposent un mécanisme faisant appel à la polygonisation des dislocations dans les régions des grains fortement déformées.

Document Type: Research Article

DOI: http://dx.doi.org/10.1179/000844374795595307

Publication date: 1974-01-01

More about this publication?

Editorial Board
Information for Authors
Submit a Paper
Subscribe to this Title
Membership Information
Information for Advertisers
Terms & Conditions
Top Articles
MSE Spotlight
Special issues
ingentaconnect is not responsible for the content or availability of external websites

Primary recrystallization during the creep of alumina

Buy & download fulltext article:

Tools

Key

Text size:

Useful pages