Authors: Ledentsov N.N.; Litvinov D.; Rosenauer A.; Gerthsen D.; Soshnikov I.P.; Shchukin V.A.; Ustinov V.M.; Egorov A.Y.u.; Zukov A.E.; Volodin V.A.; Efremov M.D.; Preobrazhenskii V.V.; Semyagin B.P.; Bimberg D.; Alferov Z.h.I.

Source: Journal of Electronic Materials, Volume 30, Number 5, May 2001 , pp. 463-470(8)

Publisher: Springer

Abstract:

GaAs-AlAs corrugated superlattices (CSL) are formed on spontaneously nanofaceted (311)A surfaces. Using high-resolution transmission electron microscopy (HRTEM) along the [233] zone axis with an appropriate image evaluation technique to enhance the contrast between GaAs and AlAs we found two distinct lateral periodicities along the [011] directions for two different CSL layer thickness regimes. For multilayer deposition with GaAs layer thickness exceeding 1 nm the lateral periodicity of 3.2 nm is clearly revealed. The contrast originates from the thickness modulation of both AlAs and GaAs layers with a period of 3.2 nm in the [011] direction. The corrugation height is about 1 nm and it is symmetric for both upper and lower GaAs-AlAs interfaces. Thicker sections of the thickness-modulated AlAs and GaAs layers of the CSL are shifted by a half period with respect to each other. In the regime when the GaAs deposited average thickness is below 1 nm, which is necessary for complete coverage of the AlAs surface, a lateral periodicity of ~1.5-2 nm is additionally revealed. We attribute this effect to the formation of local GaAs clusters dispersed on a corrugated (311)A AlAs surface resulting in a local phase reversal of the AlAs surface in their vicinity upon subsequent overgrowth. This reversal can be explained by the same effect as the phase shift of the surface corrugation upon heteroepitaxy on (311)A. In our model AlAs does not wet the GaAs cluster surface, unless different more energetically favorable scenario is possible. This causes accumulation of AlAs in the vicinity of the GaAs cluster and, as a result, the local phase reversal of the AlAs surface. The AlAs corrugated surface domains with different phases coexist on the surface resulting in an additional periodicity revealed in the HREM contrast modulation. Additionally HRTEM studies indicate that the AlAs-GaAs interface inclination angles in both regimes are 40° and 140° with respect to the flat (311) surface in an agreement with the {331} facet geometry model proposed by R. Nötzel, N.N. Ledentsov, L. Däweritz, M. Hohenstein, and K. Ploog [Phys. Rev. Lett. 67, 1812 (1991)].

Keywords: QUANTUM DOTS; CORRUGATED SUPERLATTICES; (311)A GAAS SURFACE

Document Type: Research article

Publication date: 2001-05-01

Related content

• In this: publication
• By this: publisher
• In this Subject: Materials & Manufacturing
• By this author: Ledentsov N.N. ;  Litvinov D. ;  Rosenauer A. ;  Gerthsen D. ;  Soshnikov I.P. ;  Shchukin V.A. ;  Ustinov V.M. ;  Egorov A.Y.u. ;  Zukov A.E. ;  Volodin V.A. ;  Efremov M.D. ;  Preobrazhenskii V.V. ;  Semyagin B.P. ;  Bimberg D. ;  Alferov Z.h.I.

Website © Publishing Technology. Article copyright remains with the publisher, society or author(s) as specified within the article.

• Terms and conditions
• Privacy policy
• Information for advertisers