Effect of Heat Treatment on the Drilling Performance of Aluminium/SiC MMC

Authors: Barnes S.1; Pashby I.R.1; Hashim A.B.1

Source: Applied Composite Materials, Volume 6, Number 2, March 1999 , pp. 121-138(18)

Publisher: Springer

Key:
Free Content - Free Content
New Content - New Content
Subscribed Content - Subscribed Content
Free Trial Content - Free Trial Content

Abstract:

The extremely abrasive reinforcing phases present in metal matrix composites (MMCs) are known to dominate their machining behaviour. Consequently, the properties of the matrix material are often ignored. The work reported here investigated the influence of matrix microstructure on the drilling performance of a 2618 aluminium alloy reinforced with 18% silicon carbide particles. The drills used were 8 mm diameter, titanium nitride coated K10 carbide with through-tool cooling. The workpiece material was drilled in four heat treatment conditions: as-extruded, solution treated and solution treated and aged for 12 and 20 hours. Drilling performance was assessed by measuring the wear on the drills, cutting forces, surface finish and the condition of the worn cutting edges. The results indicated that softer as-extruded and solution treated materials produced less wear and lower cutting forces than the harder aged materials. However, the height of the burrs produced during drilling were found to be greater with the softer materials and the quality of the drilled surface was also inferior. Examination of the worn cutting edges indicated that the wear mechanism was primarily one of abrasion although some attrition and edge chipping was also observed. It was concluded that when drilling these materials, the heat treatment condition of the matrix exerts a significant influence on machinability.

Keywords: drilling; metal matrix composites; cemented carbide drills; heat treatment; solution treated; aged; wear; forces; sub-surface damage

Language: English

Document Type: Regular paper

Affiliations: 1: Warwick Manufacturing Group, Department of Engineering, University of Warwick, Coventry, UK

The full text electronic article is available for purchase. You will be able to download the full text electronic article after payment.

$47.00 plus tax      Refund Policy

 

OR

Back to top

Key:
Free Content - Free Content
New Content - New Content
Subscribed Content - Subscribed Content
Free Trial Content - Free Trial Content
Share this item with others: These icons link to social bookmarking sites where readers can share and discover new web pages.
Page Help Click here for Page Help
Shopping cart
Tools
Sign in






Need to register?
Sign up here
Text size: A | A | A | A