Powder melting process for superconductor by eutectic formation

Buy Article:

$43.90 plus tax (Refund Policy)

Abstract:

with high grain alignment has been successfully fabricated by a modified powder melting process at a temperature of , which is near the eutectic point of the starting materials , and CuO. In terms of the levitation force and grain alignment, the best result was shown in a sample having a molecular ratio of 1:3:5. In the present work, the Cu-surplus eutectic liquid was completely absorbed by use of a substrate, by which the final composition was driven to stoichiometric . The results were comparable to those obtained by the conventional melt-texture-growth process. A new invariant point apparently occurred at owing to an interfacial reaction between matrix and substrate.

Document Type: Miscellaneous

Publication date: January 1, 1998

iop/sust/1998/00000011/00000007/art00005
dcterms_title,dcterms_description,pub_keyword
6
5
20
40
5

Access Key

Free Content
Free content
New Content
New content
Open Access Content
Open access content
Subscribed Content
Subscribed content
Free Trial Content
Free trial content
Cookie Policy
X
Cookie Policy
ingentaconnect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more