Grain Size‐Dependent Properties of Dense Nanocrystalline Barium Titanate Ceramics

Buy Article:

$48.00 plus tax (Refund Policy)

Abstract:

The grain size influence on the dielectric relaxation and nonlinear dielectric properties of BaTiO3 ceramics with grain size in the range of (92÷936) nm densified by Spark Plasma Sintering (SPS) from ultrafine powders were investigated. The progressive reduction of the Curie temperature and of the effective permittivity results from a combination of intrinsic size effects and low‐permittivity grain boundary layer. A model of dielectric cylindrical cavities was employed in order to calculate intrinsic effective permittivity values in GHz range. An interesting feature is the presence of a thermally activated Debye‐like relaxation in the ferroelectric state of ceramics with grain size above 300 nm, with activation energies of 0.45–0.49 eV, which seems to be related to the domain walls forced motion under the applied field. By diminishing grain size, a progressive reduction of the ferroelectric nonlinear character was obtained, reaching a macroscopic non‐switching character and a linear permittivity versus field dependence for the finest ceramics (grain size of 90–100 nm) until very high values of the applied field. The observed behavior supports the idea of frozen polarization induced by pinning centers as due to a large number of grain boundaries and charged defects in the fine structures.

Document Type: Research Article

DOI: http://dx.doi.org/10.1111/j.1551-2916.2012.05409.x

Publication date: December 1, 2012

bsc/jace/2012/00000095/00000012/art00037
dcterms_title,dcterms_description,pub_keyword
6
5
20
40
5

Access Key

Free Content
Free content
New Content
New content
Open Access Content
Open access content
Subscribed Content
Subscribed content
Free Trial Content
Free trial content
Cookie Policy
X
Cookie Policy
ingentaconnect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more