A Novel Magneto‐Dielectric Solid Solution Ceramic 0.25LiFe5O8–0.75Li2ZnTi3O8 with Relatively High Permeability and Ultra‐Low Dielectric Loss

$48.00 plus tax (Refund Policy)

Download / Buy Article:

Abstract:

In this study, a 0.25LiFe5O8–0.75Li2ZnTi3O8 solid solution ceramic was developed via the solid‐state reaction method. Its phase evolution, microstructure, and sintering behavior were investigated and it was found that the 25 mol.% LiFe5O8 phase is almost fully soluble in Li2ZnTi3O8, and only the Li2ZnTi3O8 type spinel phase was formed in the 0.25LiFe5O8–0.75Li2ZnTi3O8 ceramic. The ceramic sample sintered at 1050°C for 2 h was found to possess both good magnetic properties and dielectric properties in the frequency range from 1 to 10 MHz, with permeability between 38.2 and 15 and magnetic loss tangent between 0.25 and 0.75, permittivity between 19.6 and 19.3 and dielectric loss tangent between 8 × 10−3 and 2 × 10 3. The sample also possesses good microwave dielectric properties with a relative permittivity of 19.1, a high quality factor (Qf) ~11,770 GHz (at 6.84 GHz). The ceramic is a novel magneto‐dielectric ceramic with both high permeability and good dielectric properties, which might be a good candidate for the applications in novel electronic devices.

Document Type: Research Article

DOI: http://dx.doi.org/10.1111/jace.12075

Publication date: December 1, 2012

Related content

Tools

Favourites

Share Content

Access Key

Free Content
Free content
New Content
New content
Open Access Content
Open access content
Subscribed Content
Subscribed content
Free Trial Content
Free trial content
Cookie Policy
X
Cookie Policy
ingentaconnect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more