Effect of Simultaneous Nucleation and Crystal Growth on DSC Crystallization Peaks of Glasses

Buy Article:

$48.00 plus tax (Refund Policy)

Abstract:

In this study, the change of the height of the crystallization peak, (δT)p, and the reciprocal of the crystallization peak temperature, 1/T p, were investigated as a function of nucleation heat‐treatment time for two silicate glasses: (2BaO·TiO2·2SiO2B2TS2) and lithium disilicate (Li2O·2SiO2LS2). Then, monolithic pieces were heat‐treated in a differential scanning calorimetry furnace. The results demonstrated that these glasses behave similarly with respect to peak crystallization temperature, i.e., 1/T p decreases with the heating rate for nucleation (φn). However, the results with B2TS2 samples demonstrated that (δT)p increases with rising heating rates for nucleation (shorter nucleation heat treatment times), φn, whereas (δT)p was found to decrease with φn in the LS2 specimens. This unexpected behavior is attributed to the extensive overlapping of the I(T) and U(T) curves shown by fresnoite glass.

Document Type: Research Article

DOI: http://dx.doi.org/10.1111/j.1551-2916.2012.05333.x

Publication date: September 1, 2012

bsc/jace/2012/00000095/00000009/art00037
dcterms_title,dcterms_description,pub_keyword
6
5
20
40
5

Access Key

Free Content
Free content
New Content
New content
Open Access Content
Open access content
Subscribed Content
Subscribed content
Free Trial Content
Free trial content
Cookie Policy
X
Cookie Policy
ingentaconnect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more