Direct Coagulation Casting of Alumina Suspension by High Valence Counter Ions Using Ca(IO3)2 as Coagulating Agent

Buy Article:

$51.00 plus tax (Refund Policy)

A new direct coagulation casting of aqueous alumina suspension was developed via controlled release of high valence counter ions from calcium iodate with increase in the temperature from 55°C to 70°C. The influence of calcium iodate on the rheology of alumina suspension was investigated. A small amount of calcium iodate increased the viscosity of the concentrated alumina suspension at high temperature and finally transformed it into a wet‐coagulated body. The mechanism of coagulation is proposed such as that the solubility of calcium iodate increases with increase in temperature. The high valence Ca2+ ions diffuse into the double electrical layer of alumina particles surface through electrostatic attraction, reduces the zeta potential, hence decreases repulsive force between particles. Also reaction between Ca2+ and citrate leads to insufficient dispersant coverage on the particle surface. Both factors contribute to the coagulation of the suspension. The coagulation time was from 1 to 4 h by maintaining the temperature in the range of 55°C–70°C. The wet‐coagulated bodies prepared from 50 vol% alumina suspension showed a high compressive strength of 2.6–3.2 MPa with uniform microstructure. The relative density of sintered sample is 99.4% at 1550 °C for 2 h with perfect microstructure.
No References
No Citations
No Supplementary Data
No Data/Media
No Metrics

Document Type: Research Article

Publication date: 2012-08-01

  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more