The System Ca3(PO4)2Ca2SiO4: The Sub‐System Ca2SiO4–7CaOP2O52SiO2

Buy Article:

$51.00 plus tax (Refund Policy)

Abstract:

A study of the sub‐system Ca2SiO4–7CaOP2O52SiO2 within the system Ca3(PO4)2Ca2SiO4 was conducted as a preliminary step toward obtaining new biomaterials with controlled microstructures. Phase composition of the resulting ceramics was studied using X‐ray diffraction and scanning electron microscopy with attached wavelength dispersive spectroscopy. The results showed that the sub‐system presents an invariant eutectoid point at 518°C ± 6°C with a composition of 31 wt% Ca3(PO4)2 and 69 wt% Ca2SiO4, and typical eutectoid microstructure of lamellae morphology. These results are in disagreement with the previous reported data, which locate the invariant eutectoid point at 500 ± 20°C with a composition of 36.75 wt% Ca3(PO4)2 and 63.25 wt% Ca2SiO4.

Document Type: Research Article

DOI: http://dx.doi.org/10.1111/j.1551-2916.2011.04716.x

Publication date: December 1, 2011

bsc/jace/2011/00000094/00000012/art00061
dcterms_title,dcterms_description,pub_keyword
6
5
20
40
5

Access Key

Free Content
Free content
New Content
New content
Open Access Content
Open access content
Subscribed Content
Subscribed content
Free Trial Content
Free trial content
Cookie Policy
X
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more