Compositional Dependence of R‐curve Behavior in Soft Pb(Zr1−xTix)O3 Ceramics

Buy Article:

$43.00 plus tax (Refund Policy)

The compositional dependent fracture behavior of soft PZT (Pb0.99Ba0.01(Zr1−x Ti x )0.98Nb0.02O3) ceramics in the vicinity of the morphotropic phase boundary was characterized using compact‐tension specimens. The compositions with 0.40 ≤ x ≤ 0.55 displayed an increasing fracture resistance with crack extension (R‐curve behavior). It was observed that the rhombohedral composition and the compositions near the morphotropic phase boundary showed the largest toughness enhancement. R‐curve behavior was found to be influenced by the ferroelastic coercive stress, saturated remanent strain, and elastic modulus, which were experimentally measured for each composition. X‐ray diffraction measurements were performed and compared to the fracture results to investigate the impact of phase and lattice distortion on ferroelastic toughening behavior.
No References
No Citations
No Supplementary Data
No Article Media
No Metrics

Document Type: Research Article

Publication date: 01 December 2011

  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more