High Heat Generation Ability in AC Magnetic Field of Y3Fe5O12 Powder Prepared Using Bead Milling

Buy Article:

$43.00 plus tax (Refund Policy)

We found that the nano‐sized Y3Fe5O12 powder prepared by bead milling has the highest heat generation ability in an AC magnetic field of reported superparamagnetic materials. The heat generation ability in an AC magnetic field was strongly improved by a decrease in the average crystallite size of the bead milled samples. The highest heat ability in the AC magnetic field was for the fine Y3Fe5O12 powder with ca. 15 nm crystallite size (the samples milled for 4 h using 0.1 mmφ beads). The reasons for the high heat generation properties of the milled samples are ascribed to an increase in the Néel relaxation of the superparamagnetic material. The heat generation ability (W·g−1) can be estimated using a 3.58 × 10−4 f·H2 frequency (f/kHz) and the magnetic field (H/kA·m−1) for the sample milled for 4 h using 0.1 mmφ beads.
No References
No Citations
No Supplementary Data
No Article Media
No Metrics

Document Type: Research Article

Publication date: 01 December 2011

  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more