Large Electric‐Field Induced Strain in BiFeO3 Ceramics

$48.00 plus tax (Refund Policy)

Download / Buy Article:

Abstract:

Large bipolar strain of up to 0.36% (peak‐to‐peak value) was measured in BiFeO3 ceramics at low frequency (0.1 Hz) and large amplitude (140 kV/cm) of the driving field. This strain is comparable to that achievable in highly efficient morphotropic phase boundary (MPB) Pb‐based perovskite ceramics, such as Pb(Zr,Ti)O3 and Pb(Mg,Nb)O3–PbTiO3. The strain showed a strong dependence on the field frequency, and is probably largely associated with domain switching involving predominantly non‐180° domain walls. In addition, application of an electric field of low frequency rearranges the defects, which act as pinning centers for the domain walls. The resulting depinning of the domain walls leads to a more efficient switching and, consequently, to an increased response. The large strain reported here suggests that the domain‐wall motion in BiFeO3 may be as large as in classical lead‐based ferroelectrics. We hope that this finding might further stimulate the search of new lead‐free MPB compositions based on BiFeO3.

Document Type: Research Article

DOI: http://dx.doi.org/10.1111/j.1551-2916.2011.04861.x

Publication date: December 1, 2011

Related content

Tools

Favourites

Share Content

Access Key

Free Content
Free content
New Content
New content
Open Access Content
Open access content
Subscribed Content
Subscribed content
Free Trial Content
Free trial content
Cookie Policy
X
Cookie Policy
ingentaconnect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more