Fabrication of Transparent Y2Zr2O7 Ceramics from Combustion-Synthesized Powders

Buy Article:

$51.00 plus tax (Refund Policy)


Y2Zr2O7 transparent ceramic was successfully fabricated from combustion-synthesized powders. The as-prepared Y2Zr2O7 powders were characterized by XRD, FE-SEM, TEM, and BET area. After high-energy ball milling, the porous structure of the powder was destroyed. The Y2Zr2O7 transparent ceramics were obtained by sintering the ball-milled powders at 1850°C for 6 h in vacuum. Ball milling of the as-burnt powders was found to play a key role on the in-line transmittance of the resultant ceramic.

Document Type: Research Article


Affiliations: SCHOTT Glass Technologies (Suzhou) Co. Ltd., Suzhou 215009, China

Publication date: 2011-04-01

  • Access Key
  • Free content
  • Partial Free content
  • New content
  • Open access content
  • Partial Open access content
  • Subscribed content
  • Partial Subscribed content
  • Free trial content
Cookie Policy
Cookie Policy
Ingenta Connect website makes use of cookies so as to keep track of data that you have filled in. I am Happy with this Find out more